POM 美国杜邦 107 热稳定 耐磨 高刚性 高流动 包装容器 运动器材

商品描述

 

产品参数

性能项目试验条件[状态]测试方法测试数据数据单位其它性能弯曲降服强度+73℉ASTM D-79014.3MPsi基本性能密度
ASTM D-7921.42
物理性能吸水量E R.h.+73℉(+23℃)ASTM D-5700.22
吸水量24hrs浸泡+73℉(+23℃)ASTM D-5700.25
吸水量浸泡均衡点+73℉(+23℃)ASTM D-5700.90
扩散因数+73℉(+23℃)106HzASTM D-1500.005
机械性能摩擦系数+73℉(+23℃)动态ThrustWasherTest30.35
挠曲系数+70℃在25℃下1550MPa挠曲系数-55℃在25℃下3650MPa断裂时之拉力伸张度+73℉(+23℃)ASTM D-63875
挠曲系数+158℉在25℃下225MPsi伸张强度+212℉ASTM D-6385.2MPsi断裂时之拉力伸张度+212℉(+100℃)ASTM D-638>260
IZOD冲击强度+73℉ASTM D-2562.3ft.lb/in伸张强度+250℉ASTM D-6383.8MPsi伸张强度-68℉ASTM D-63814.7MPsi挠曲系数+212℉在25℃下130MPsi挠曲系数-68℉在25℃下530MPsi挠曲系数+250℉在25℃下90MPsi拉力冲击抵抗力+73℉D1822Long170ft.lb/in2拉力冲击抵抗力+23℃D1822Long350kj/m2剪力+23℃ASTM D-73265.5MPa挠曲系数+73℉在25℃下380MPsi剪力+73℉ASTM D-7329.5MPsi挠曲系数+100℃25℃下895MPa弯曲疲劳忍耐限度+73℉ASTM D-6714.7MPsi伸张强度+100℃ASTM D-63835.9MPa断裂时之拉力伸张度+250℉(+122℃)ASTM D-638>260
断裂时之拉力伸张度+158℉(+70℃)ASTM D-638230 
无切口冲击程度+73℉ASTM D-256>100(no break)ft.lb/in弯曲降服强度+23℃ASTM D-79098.6MPa压缩应力+23℃@1 Def.ASTM D-69535.9MPa伸张强度-55℃ASTM D-638101MPa挠曲系数+23℃在25℃下2620MPa伸张强度+73℉ASTM D-63810.0MPsi压缩应力+73℉@10 DefASTM D-69518.0MPsi伸张强度+122℃ASTM D-63826.2MPa压缩应力+23℃@10 Def.ASTM D-695124MPa伸张强度+70℃ASTM D-6386.9MPa弯曲疲劳忍耐限度+23℃ASTM D-67132.4MPaIZOD冲击强度40℃ASTM D-25696.1j/m伸张强度+158℉ASTM D-6386.9MPsiIZOD冲击强度-40℉ASTM D-2561.8ft.lb/in洛氏硬度
ASTM D-785M94,R120
挠曲系数+122℃在25℃下620MPa弹性系数+73℉ASTM D-638450MPsi摩擦系数+73℉(+23℃)静态ThrustWasherTest30.20
弹性系数+23℃ASTM D-6383100MPa断裂时之拉力伸张度-68℉(-55℃)ASTM D-63838
负载下之变形2000psi@+122℉(14Mpa@50℃)ASTM D-6210.5
伸张强度+23℃ASTM D-63868.9MPa无切口冲击程度+23℃ASTM D-256>5300(no break)j/mIZOD冲击强度+23℃ASTM D-256123j/m压缩应力+73℉@1 Def.ASTM D-6955.2MPsi电气性能绝缘强度Short Time,2.3mmASTM D-14919.7MV/m绝缘系数+73℉(+23℃)102to106HzASTM D-1503.7
电弧抵抗力120mil(3.1mm)ASTM D-495220no trackingSec.绝缘强度Short Time,90 milsASTM D-149500V/mil电阻系数+73℉(+23℃)0.2 H2OASTM D-2571015ohm-cm热性能可燃烧性
UL-9494HB
线性热膨胀系数-40 to +85℉ASTM D-6965.810-5in/in.℉线性热膨胀系数+220 to +300℉ASTM D-6968.310-5in/in.℉热变形温度0.5MPaASTM D-648172℃线性热膨胀系数-40 to +29℃ASTM D-69610.410-5m/m.℃热传导系数

2.6BTU-in/hr线性热膨胀系数+60 to +104℃ASTM D-69613.710-5m/m.℃热变形温度1.8MPaASTM D-648136℃热变形温度66psiASTM D-648342℉熔点
ASTM D-2133175℃热变形温度264psiASTM D-648277℉熔点
ASTM D-2133347℉线性热膨胀系数+29 to +60℃ASTM D-69612.210-5m/m.℃线性热膨胀系数+104 to +150℃ASTM D-69614.910-5m/m.℃线性热膨胀系数+85 to +140℉ASTM D-6966.810-5in/in.℉线性热膨胀系数+140 to +220℉ASTM D-6967.610-5in/in.℉热传导系数

0.37W/mk

DELRIN聚甲醛产品具有独特的粘接强度、硬度、不易弯曲、尺寸稳定性、韧性、耐疲劳性、耐溶剂、阻燃、抗磨损、耐用、低摩擦等特点，因此，它可以被用来填补金属和一般塑料之间的不足。

POM（聚甲醛树脂）定义：聚甲醛是一种没有侧链、高密度、高结晶性的线型聚合物。按其分子链中化学结构的不同，可分为均聚甲醛和共聚甲醛两种。两者的重要区别是：均聚甲醛密度、结晶度、熔点都高，但热稳定性差，加工温度范围窄（约10℃），对酸碱稳定性略低；而共聚甲醛密度、结晶度、熔点、强度都较低，但热稳定性好，不易分解，加工温度范围宽（约50℃），对酸碱稳定性较好。是具有优异的综合性能的工程塑料。有良好的物理、机械和化学性能，尤其是有优异的耐摩擦性能。俗称赛钢或夺钢，为第三大通用塑料。适于制作减磨耐磨零件，传动零件，以及化工，仪表等零件。