POM美国杜邦1700P-POM 1700P物性表
发布时间：2023-10-30 浏览次数：11
返回列表
1700P 物性表
机械性能额定值单位测试方法
| 破裂点拉伸变形量 (100℃) | >260 |
| ASTM D-638 |
| 挠曲变形强度 (23℃) | 103 | MPa | ASTM D-790 |
| 拉伸强度 (122℃) | 26 | MPa | ASTM D-638 |
| 压缩应力 (23℃,10%变形) | 106 | MPa | ASTM D-695 |
| 负载变形量 (140kg/cm,50℃) | 0.9 | % | ASTM D-621 |
| IZOD冲击试验 (23℃) | 59 | j/m | ASTM D-256 |
| 破裂点拉伸变形量 (23℃) | 15 | % | ASTM D-638 |
| 抗剪强度 (23℃) | 58 | MPa | ASTM D-732 |
| 破裂点拉伸变形量 (122℃) | >260 | % | ASTM D-638 |
| 挠曲系数 (23℃) | 3230 | MPa | ASTM D-790 |
| 破裂点拉伸变形量 (-55℃) | 10 | % | ASTM D-638 |
| 挠曲系数 (100℃) | 1080 | MPa | ASTM D-790 |
| 拉伸强度 (23℃) | 70 | MPa | ASTM D-638 |
| 洛氏硬度 | 107 | R scale | ASTM D-785 |
| 挠曲系数 (122℃) | 755 | MPa | ASTM D-790 |
| 拉伸强度 (-55℃) | 103 | MPa | ASTM D-638 |
| 挠曲系数 |
|
| ASTM D-790 |
| (-55℃) | 4750 | MPa |
|
| (70℃) | 1740 | MPa |
|
| 拉伸强度 |
|
| ASTM D-638 |
| (100℃) | 36 | MPa |
|
| (70℃) | 48 | MPa |
|
| 压缩应力 (23℃,1%变形) | 22 | MPa | ASTM D-695 |
| IZOD冲击试验 (缺口-40℃) | 52 | j/m | ASTM D-256 |
| 洛氏硬度 | 89 | M scale | ASTM D-785 |
核心提示：1700P物性,POM1700P,杜邦1700P