GH-20
POM | 聚甲醛#赛钢日本宝理规格级别： 增强
GH-20 物性表
| 比重 | 1.54 | g/cm | ASTM D792,ISO 1183 |
| 屈服拉伸应力 | |||
| 100 | MPa | ISO 527-2 | |
| 108 | MPa | ASTM D638 | |
| 断裂伸长率 | |||
| 3.0 | % | ASTM D638 | |
| 2.0 | % | ISO 527-2 | |
| 弯曲模量 | |||
| 6470 | MPa | ASTM D790 | |
| 6000 | MPa | ISO 178 | |
| 弯曲强度 | |||
| 167 | MPa | ASTM D790 | |
| 135 | MPa | ISO 178 | |
| CHARPY缺口冲击强度 | 5.2 | KJ/m | ISO 179/1eA |
| 缺口冲击强度 | 54 | J/m | ASTM D256 |
| Reverse缺口冲击强度 | 440 | J/m | ASTM D256 |
| 热变形温度 | |||
| (1.8MPa,未退火) | 162 | ℃ | ASTM D648 |
| (1.8MPa,未退火) | 158 | ℃ | ISO 75-2/A |
| 阻燃等级 | HB | UL 94 | |
| 颜色数 | CF3500 |