M90-35
POM | 聚甲醛#赛钢日本宝理规格级别： 耐候
备注说明： 良好的耐候性
M90-35 物性表
| 比重 | 1.41 | g/cm | ASTM D792,ISO 1183 |
| 屈服拉伸应力 | |||
| 62 | MPa | ISO 527-2 | |
| 61 | MPa | ASTM D638 | |
| 断裂伸长率 | |||
| 60 | % | ASTM D638 | |
| 35 | % | ISO 527-2 | |
| 弯曲模量 | |||
| 2590 | MPa | ASTM D790 | |
| 2500 | MPa | ISO 178 | |
| 弯曲强度 | |||
| 96 | MPa | ASTM D790 | |
| 87 | MPa | ISO 178 | |
| CHARPY缺口冲击强度 | 6 | KJ/m | ISO 179/1eA |
| 缺口冲击强度 | 64 | J/m | ASTM D256 |
| Reverse缺口冲击强度 | 760 | J/m | ASTM D256 |
| 热变形温度 | |||
| (1.8MPa,未退火) | 110 | ℃ | ASTM D648 |
| (1.8MPa,未退火) | 95 | ℃ | ISO 75-2/A |
| 阻燃等级 | HB | UL 94 |