DuPont Performance Polymers Zytel® HTN 51G35HSLR BK420 Polyphthalamide (PPA) (Unverified Data**) 物性表

物理性能额定值 (公制)额定值 (英制)测试方法密度1.47 g/cc0.0531 lb/in³DAM; ISO 1183线性成型收缩率,Flow0.0020 cm/cm0.0020 in/inDAM; ISO 294-4 2577线性成型收缩率，横向0.0060 cm/cm0.0060 in/inDAM; ISO 294-4 2577机械性能额定值 (公制)额定值 (英制)测试方法球压硬度310 MPa45000 psiDAM; H 961/30; ISO 2039-1抗张强度(断裂)190 MPa27600 psi50%RH; ISO 527-1/-2
200 MPa29000 psiDAM; ISO 527-1/-2抗张强度11.35 MPa

@Strain 0.100 %, Temperature 23.0 °C

1646 psi

@Strain 0.100 %, Temperature 73.4 °F

DAM; ISO 11403-1 -2
17.63 MPa

@Strain 0.300 %, Temperature 150 °C

2557 psi

@Strain 0.300 %, Temperature 302 °F

DAM; ISO 11403-1 -2
43.48 MPa

@Strain 0.800 %, Temperature 150 °C

6306 psi

@Strain 0.800 %, Temperature 302 °F

DAM; ISO 11403-1 -2
54.0 MPa

@Strain 1.10 %, Temperature 150 °C

7830 psi

@Strain 1.10 %, Temperature 302 °F

DAM; ISO 11403-1 -2
64.12 MPa

@Strain 0.500 %, Temperature -40.0 °C

9300 psi

@Strain 0.500 %, Temperature -40.0 °F

DAM; ISO 11403-1 -2
65.54 MPa

@Strain 1.60 %, Temperature 150 °C

9506 psi

@Strain 1.60 %, Temperature 302 °F

DAM; ISO 11403-1 -2
66.07 MPa

@Strain 0.600 %, Temperature 23.0 °C

9583 psi

@Strain 0.600 %, Temperature 73.4 °F

DAM; ISO 11403-1 -2
96.19 MPa

@Strain 0.900 %, Temperature 23.0 °C

13950 psi

@Strain 0.900 %, Temperature 73.4 °F

DAM; ISO 11403-1 -2
96.76 MPa

@Strain 0.800 %, Temperature -40.0 °C

14030 psi

@Strain 0.800 %, Temperature -40.0 °F

DAM; ISO 11403-1 -2
130.11 MPa

@Strain 1.30 %, Temperature 23.0 °C

18871 psi

@Strain 1.30 %, Temperature 73.4 °F

DAM; ISO 11403-1 -2
144.37 MPa

@Strain 1.30 %, Temperature -40.0 °C

20939 psi

@Strain 1.30 %, Temperature -40.0 °F

DAM; ISO 11403-1 -2
176.86 MPa

@Strain 1.70 %, Temperature -40.0 °C

25651 psi

@Strain 1.70 %, Temperature -40.0 °F

DAM; ISO 11403-1 -2
190.97 MPa

@Strain 2.30 %, Temperature 23.0 °C

27698 psi

@Strain 2.30 %, Temperature 73.4 °F

DAM; ISO 11403-1 -2伸长率 (断裂)2.0 %2.0 %50%RH; ISO 527-1/-2
2.3 %2.3 %DAM; ISO 527-1/-2拉伸模量11.5 GPa1670 ksiDAM; ISO 527-1/-2
11.5 GPa1670 ksi50%RH; ISO 527-1/-2弯曲模量10.5 GPa1520 ksiDAM; ISO 178割线模量6.36 GPa

@Strain 2.30 %, Temperature 100 °C

923 ksi

@Strain 2.30 %, Temperature 212 °F

DAM; ISO 11403-1 -2
7.10 GPa

@Strain 1.90 %, Temperature 100 °C

1030 ksi

@Strain 1.90 %, Temperature 212 °F

DAM; ISO 11403-1 -2
7.774 GPa

@Strain 1.50 %, Temperature 100 °C

1128 ksi

@Strain 1.50 %, Temperature 212 °F

DAM; ISO 11403-1 -2
8.387 GPa

@Strain 1.00 %, Temperature 100 °C

1216 ksi

@Strain 1.00 %, Temperature 212 °F

DAM; ISO 11403-1 -2
8.64 GPa

@Strain 0.300 %, Temperature 100 °C

1250 ksi

@Strain 0.300 %, Temperature 212 °F

DAM; ISO 11403-1 -2
8.833 GPa

@Strain 2.00 %, Temperature 23.0 °C

1281 ksi

@Strain 2.00 %, Temperature 73.4 °F

DAM; ISO 11403-1 -2
9.2125 GPa

@Strain 2.40 %, Temperature -40.0 °C

1336.2 ksi

@Strain 2.40 %, Temperature -40.0 °F

DAM; ISO 11403-1 -2
9.67 GPa

@Strain 1.50 %, Temperature 23.0 °C

1400 ksi

@Strain 1.50 %, Temperature 73.4 °F

DAM; ISO 11403-1 -2
9.898 GPa

@Strain 2.00 %, Temperature -40.0 °C

1436 ksi

@Strain 2.00 %, Temperature -40.0 °F

DAM; ISO 11403-1 -2
10.527 GPa

@Strain 1.00 %, Temperature 23.0 °C

1526.8 ksi

@Strain 1.00 %, Temperature 73.4 °F

DAM; ISO 11403-1 -2
10.9 GPa

@Strain 1.40 %, Temperature -40.0 °C

1580 ksi

@Strain 1.40 %, Temperature -40.0 °F

DAM; ISO 11403-1 -2
11.0 GPa

@Strain 0.600 %, Temperature 23.0 °C

1600 ksi

@Strain 0.600 %, Temperature 73.4 °F

DAM; ISO 11403-1 -2
11.35 GPa

@Strain 0.100 %, Temperature 23.0 °C

1646 ksi

@Strain 0.100 %, Temperature 73.4 °F

DAM; ISO 11403-1 -2
12.095 GPa

@Strain 0.800 %, Temperature -40.0 °C

1754.3 ksi

@Strain 0.800 %, Temperature -40.0 °F

DAM; ISO 11403-1 -2
12.824 GPa

@Strain 0.500 %, Temperature -40.0 °C

1860.0 ksi

@Strain 0.500 %, Temperature -40.0 °F

DAM; ISO 11403-1 -2简支梁无缺口冲击强度3.50 J/cm²16.7 ft-lb/in²50%RH; ISO 179/1eU
5.00 J/cm²23.8 ft-lb/in²DAM; ISO 179/1eU简支梁缺口冲击强度0.800 J/cm²3.81 ft-lb/in²50%RH; ISO 179/1eA
0.900 J/cm²4.28 ft-lb/in²DAM; ISO 179/1eA电气性能额定值 (公制)额定值 (英制)测试方法体积电阻率1.00e+15 ohm-cm1.00e+15 ohm-cmDAM; IEC 60093介电强度33.0 kV/mm838 kV/in50%RH; IEC 60243-1
34.0 kV/mm864 kV/inDAM; IEC 60243-1热性能额定值 (公制)额定值 (英制)测试方法线形热膨胀系数 - 流动20.0 µm/m-°C11.1 µin/in-°FDAM; ISO 11359-1/-2
20.0 µm/m-°C

@Temperature -40.0 - 23.0 °C

11.1 µin/in-°F

@Temperature -40.0 - 73.4 °F

DAM; ISO 11359-1/-2线性热膨胀系数,横向流动58.0 µm/m-°C32.2 µin/in-°FDAM; ISO 11359-1/-2
55.0 µm/m-°C

@Temperature -40.0 - 23.0 °C

30.6 µin/in-°F

@Temperature -40.0 - 73.4 °F

DAM; ISO 11359-1/-2熔融温度300 °C572 °FDAM; first heat; ISO 11357-1/-3载荷下热变形温度(0.46 MPa)276 °C529 °FDAM; ISO 75-1/-2载荷下热变形温度(1.8 MPa)262 °C504 °FDAM; ISO 75-1/-2Flame Spread28 mm/min

@Thickness 1.00 mm

1.1 in/min

@Thickness 0.0394 in

ISO 3795 (FMVSS 302)材料描述
测试方法AdditivesLubricants

Release agent
Delivery FormPellets
部件标识代码>PA6T/XT-GF35<ISO 11469
>PPA-GF35<SAE J1344加工Injection Moulding
供货地区Asia Pacific

Europe

Global

Near East/Africa

North America

South and Central America
特殊特性Heat stabilised or stable to heat