DuPont Performance Polymers Zytel® 135F NC010 Nylon 66 (Unverified Data**) 物性表

物理性能额定值 (公制)额定值 (英制)测试方法密度1.01 g/cc0.0365 lb/in³

1.14 g/cc0.0412 lb/in³DAM; ISO 1183吸水率8.5 %

@Thickness 2.00 mm

8.5 %

@Thickness 0.0787 in

DAM; Sim. to ISO 62水分吸收2.70 %

@Thickness 2.00 mm

2.70 %

@Thickness 0.0787 in

DAM; Sim. to ISO 62粘度64000 cP

@Shear Rate 5000 1/s, Temperature 315 °C

64000 cP

@Shear Rate 5000 1/s, Temperature 599 °F

ISO 11403-1 -2
83000 cP

@Shear Rate 5000 1/s, Temperature 295 °C

83000 cP

@Shear Rate 5000 1/s, Temperature 563 °F

ISO 11403-1 -2
105000 cP

@Shear Rate 5000 1/s, Temperature 275 °C

105000 cP

@Shear Rate 5000 1/s, Temperature 527 °F

ISO 11403-1 -2
134000 cP

@Shear Rate 500 1/s, Temperature 315 °C

134000 cP

@Shear Rate 500 1/s, Temperature 599 °F

ISO 11403-1 -2
195000 cP

@Shear Rate 500 1/s, Temperature 295 °C

195000 cP

@Shear Rate 500 1/s, Temperature 563 °F

ISO 11403-1 -2
284000 cP

@Shear Rate 500 1/s, Temperature 275 °C

284000 cP

@Shear Rate 500 1/s, Temperature 527 °F

ISO 11403-1 -2粘度测试150 cm³/g150 cm³/gDAM; ISO 307 1157 1628线性成型收缩率,Flow0.0070 cm/cm0.0070 in/inDAM; ISO 294-4 2577线性成型收缩率，横向0.013 cm/cm0.013 in/inDAM; ISO 294-4 2577机械性能额定值 (公制)额定值 (英制)测试方法洛氏硬度（M 级）646450%RH; ISO 2039-2
8787DAM; ISO 2039-2洛氏硬度（R 级）11611650%RH; ISO 2039-2
123123DAM; ISO 2039-2抗张强度7.47 MPa

@Strain 0.960 %, Temperature 90.0 °C

1080 psi

@Strain 0.960 %, Temperature 194 °F

DAM; ISO 11403-1 -2
11.4 MPa

@Strain 0.480 %, Temperature 40.0 °C

1650 psi

@Strain 0.480 %, Temperature 104 °F

DAM; ISO 11403-1 -2
17.8 MPa

@Strain 2.40 %, Temperature 90.0 °C

2580 psi

@Strain 2.40 %, Temperature 194 °F

DAM; ISO 11403-1 -2
18.0 MPa

@Strain 0.480 %, Temperature 23.0 °C

2610 psi

@Strain 0.480 %, Temperature 73.4 °F

DAM; ISO 11403-1 -2
22.8 MPa

@Strain 0.550 %, Temperature 0.000 °C

3310 psi

@Strain 0.550 %, Temperature 32.0 °F

DAM; ISO 11403-1 -2
24.5 MPa

@Strain 3.84 %, Temperature 90.0 °C

3550 psi

@Strain 3.84 %, Temperature 194 °F

DAM; ISO 11403-1 -2
26.5 MPa

@Strain 0.630 %, Temperature -20.0 °C

3840 psi

@Strain 0.630 %, Temperature -4.00 °F

DAM; ISO 11403-1 -2
41.6 MPa

@Strain 1.92 %, Temperature 40.0 °C

6030 psi

@Strain 1.92 %, Temperature 104 °F

DAM; ISO 11403-1 -2
60.5 MPa

@Strain 3.36 %, Temperature 40.0 °C

8770 psi

@Strain 3.36 %, Temperature 104 °F

DAM; ISO 11403-1 -2
65.5 MPa

@Strain 1.92 %, Temperature 23.0 °C

9500 psi

@Strain 1.92 %, Temperature 73.4 °F

DAM; ISO 11403-1 -2
65.7 MPa

@Strain 4.80 %, Temperature 40.0 °C

9530 psi

@Strain 4.80 %, Temperature 104 °F

DAM; ISO 11403-1 -2
82.7 MPa

@Strain 2.20 %, Temperature 0.000 °C

12000 psi

@Strain 2.20 %, Temperature 32.0 °F

DAM; ISO 11403-1 -2
92.9 MPa

@Strain 3.36 %, Temperature 23.0 °C

13500 psi

@Strain 3.36 %, Temperature 73.4 °F

DAM; ISO 11403-1 -2
95.4 MPa

@Strain 2.52 %, Temperature -20.0 °C

13800 psi

@Strain 2.52 %, Temperature -4.00 °F

DAM; ISO 11403-1 -2
117 MPa

@Strain 3.85 %, Temperature 0.000 °C

17000 psi

@Strain 3.85 %, Temperature 32.0 °F

DAM; ISO 11403-1 -2
133 MPa

@Strain 4.41 %, Temperature -20.0 °C

19300 psi

@Strain 4.41 %, Temperature -4.00 °F

DAM; ISO 11403-1 -2
3.00 MPa

@Strain 0.165 %, Time 36000 sec

435 psi

@Strain 0.165 %, Time 10.0 hour

50%RH; isochronous; ISO 11403-1 -2
3.00 MPa

@Strain 0.192 %, Time 360000 sec

435 psi

@Strain 0.192 %, Time 100 hour

50%RH; isochronous; ISO 11403-1 -2
3.00 MPa

@Strain 0.231 %, Time 3.60e+6 sec

435 psi

@Strain 0.231 %, Time 1000 hour

50%RH; isochronous; ISO 11403-1 -2
3.00 MPa

@Strain 0.146 %, Time 3600 sec

435 psi

@Strain 0.146 %, Time 1.00 hour

50%RH; isochronous; ISO 11403-1 -2
3.00 MPa

@Strain 0.297 %, Time 3.60e+7 sec

435 psi

@Strain 0.297 %, Time 10000 hour

50%RH; isochronous; ISO 11403-1 -2
12.0 MPa

@Strain 1.45 %, Time 3.60e+7 sec

1740 psi

@Strain 1.45 %, Time 10000 hour

50%RH; isochronous; ISO 11403-1 -2
12.0 MPa

@Strain 0.656 %, Time 3600 sec

1740 psi

@Strain 0.656 %, Time 1.00 hour

50%RH; isochronous; ISO 11403-1 -2
12.0 MPa

@Strain 1.18 %, Time 3.60e+6 sec

1740 psi

@Strain 1.18 %, Time 1000 hour

50%RH; isochronous; ISO 11403-1 -2
12.0 MPa

@Strain 0.947 %, Time 360000 sec

1740 psi

@Strain 0.947 %, Time 100 hour

50%RH; isochronous; ISO 11403-1 -2
12.0 MPa

@Strain 0.772 %, Time 36000 sec

1740 psi

@Strain 0.772 %, Time 10.0 hour

50%RH; isochronous; ISO 11403-1 -2抗张强度(屈服)67.0 MPa9720 psi50%RH; ISO 527-1/-2
96.0 MPa13900 psiDAM; ISO 527-1/-2伸长率 (断裂)13 %13 %DAM; Nominal; ISO 527-1/-2
50 %50 %50%RH; Nominal; ISO 527-1/-2屈服伸长率4.5 %4.5 %DAM; ISO 527-1/-2
4.5 %4.5 %DAM; ISO 527-3
18 %18 %50%RH; ISO 527-1/-2拉伸模量2.00 GPa290 ksi50%RH; ISO 527-1/-2
3.60 GPa522 ksiDAM; ISO 527-1/-2剪切模量0.175 GPa

@Temperature 160 °C

25.4 ksi

@Temperature 320 °F

DAM; Dynamic; ISO 11403-1 -2
0.214 GPa

@Temperature 120 °C

31.0 ksi

@Temperature 248 °F

DAM; Dynamic; ISO 11403-1 -2
0.449 GPa

@Temperature 70.0 °C

65.1 ksi

@Temperature 158 °F

DAM; Dynamic; ISO 11403-1 -2
1.0685 GPa

@Temperature 20.0 °C

154.98 ksi

@Temperature 68.0 °F

DAM; Dynamic; ISO 11403-1 -2
1.171 GPa

@Temperature -20.0 °C

169.8 ksi

@Temperature -4.00 °F

DAM; Dynamic; ISO 11403-1 -2
1.259 GPa

@Temperature -50.0 °C

182.6 ksi

@Temperature -58.0 °F

DAM; Dynamic; ISO 11403-1 -2抗剪强度0.0670 MPa

@Shear Rate 500 1/s, Temperature 315 °C

9.72 psi

@Shear Rate 500 1/s, Temperature 599 °F

ISO 11403-1 -2
0.0975 MPa

@Shear Rate 500 1/s, Temperature 295 °C

14.1 psi

@Shear Rate 500 1/s, Temperature 563 °F

ISO 11403-1 -2
0.142 MPa

@Shear Rate 500 1/s, Temperature 275 °C

20.6 psi

@Shear Rate 500 1/s, Temperature 527 °F

ISO 11403-1 -2割线模量1.66 GPa

@Strain 3.84 %, Temperature 40.0 °C

240 ksi

@Strain 3.84 %, Temperature 104 °F

DAM; ISO 11403-1 -2
2.17 GPa

@Strain 1.92 %, Temperature 40.0 °C

314 ksi

@Strain 1.92 %, Temperature 104 °F

DAM; ISO 11403-1 -2
2.375 GPa

@Strain 0.480 %, Temperature 40.0 °C

344.5 ksi

@Strain 0.480 %, Temperature 104 °F

DAM; ISO 11403-1 -2
2.52 GPa

@Strain 3.84 %, Temperature 23.0 °C

365 ksi

@Strain 3.84 %, Temperature 73.4 °F

DAM; ISO 11403-1 -2
2.7381 GPa

@Strain 5.04 %, Temperature -20.0 °C

397.13 ksi

@Strain 5.04 %, Temperature -4.00 °F

DAM; ISO 11403-1 -2
2.77 GPa

@Strain 4.40 %, Temperature 0.000 °C

402 ksi

@Strain 4.40 %, Temperature 32.0 °F

DAM; ISO 11403-1 -2
3.41 GPa

@Strain 1.92 %, Temperature 23.0 °C

495 ksi

@Strain 1.92 %, Temperature 73.4 °F

DAM; ISO 11403-1 -2