DuPont Performance Polymers Zytel® HTN 51G35HSL BK083 Polyphthalamide (PPA) (Unverified Data**) 物性表

物理性能额定值 (公制)额定值 (英制)测试方法密度1.47 g/cc0.0531 lb/in³DAM; ISO 1183线性成型收缩率,Flow0.0020 cm/cm0.0020 in/inDAM; ISO 294-4 2577线性成型收缩率，横向0.0060 cm/cm0.0060 in/inDAM; ISO 294-4 2577机械性能额定值 (公制)额定值 (英制)测试方法抗张强度(断裂)200 MPa29000 psi50%RH; ISO 527-1/-2
210 MPa30500 psiDAM; ISO 527-1/-2抗张强度8.88 MPa

@Strain 0.190 %, Temperature 150 °C

1290 psi

@Strain 0.190 %, Temperature 302 °F

50%RH; ISO 11403-1 -2
12.91 MPa

@Strain 0.280 %, Temperature 180 °C

1872 psi

@Strain 0.280 %, Temperature 356 °F

DAM; ISO 11403-1 -2
20.41 MPa

@Strain 0.360 %, Temperature 150 °C

2960 psi

@Strain 0.360 %, Temperature 302 °F

DAM; ISO 11403-1 -2
24.59 MPa

@Strain 0.650 %, Temperature 150 °C

3566 psi

@Strain 0.650 %, Temperature 302 °F

50%RH; ISO 11403-1 -2
38.11 MPa

@Strain 1.15 %, Temperature 180 °C

5527 psi

@Strain 1.15 %, Temperature 356 °F

DAM; ISO 11403-1 -2
38.35 MPa

@Strain 1.40 %, Temperature 150 °C

5562 psi

@Strain 1.40 %, Temperature 302 °F

50%RH; ISO 11403-1 -2
40.83 MPa

@Strain 0.550 %, Temperature 90.0 °C

5922 psi

@Strain 0.550 %, Temperature 194 °F

50%RH; ISO 11403-1 -2
46.25 MPa

@Strain 2.23 %, Temperature 150 °C

6708 psi

@Strain 2.23 %, Temperature 302 °F

50%RH; ISO 11403-1 -2
48.71 MPa

@Strain 1.24 %, Temperature 150 °C

7065 psi

@Strain 1.24 %, Temperature 302 °F

DAM; ISO 11403-1 -2
48.84 MPa

@Strain 2.11 %, Temperature 180 °C

7084 psi

@Strain 2.11 %, Temperature 356 °F

DAM; ISO 11403-1 -2
55.6 MPa

@Strain 3.25 %, Temperature 180 °C

8060 psi

@Strain 3.25 %, Temperature 356 °F

DAM; ISO 11403-1 -2
60.42 MPa

@Strain 2.38 %, Temperature 150 °C

8763 psi

@Strain 2.38 %, Temperature 302 °F

DAM; ISO 11403-1 -2
65.19 MPa

@Strain 0.600 %, Temperature 90.0 °C

9455 psi

@Strain 0.600 %, Temperature 194 °F

DAM; ISO 11403-1 -2
66.06 MPa

@Strain 1.14 %, Temperature 90.0 °C

9581 psi

@Strain 1.14 %, Temperature 194 °F

50%RH; ISO 11403-1 -2
66.18 MPa

@Strain 3.75 %, Temperature 150 °C

9599 psi

@Strain 3.75 %, Temperature 302 °F

DAM; ISO 11403-1 -2
73.19 MPa

@Strain 0.620 %, Temperature 40.0 °C

10620 psi

@Strain 0.620 %, Temperature 104 °F

DAM; ISO 11403-1 -2
80.45 MPa

@Strain 1.80 %, Temperature 90.0 °C

11670 psi

@Strain 1.80 %, Temperature 194 °F

50%RH; ISO 11403-1 -2
83.19 MPa

@Strain 0.720 %, Temperature 23.0 °C

12070 psi

@Strain 0.720 %, Temperature 73.4 °F

50%RH; ISO 11403-1 -2
88.89 MPa

@Strain 2.62 %, Temperature 90.0 °C

12890 psi

@Strain 2.62 %, Temperature 194 °F

50%RH; ISO 11403-1 -2
91.36 MPa

@Strain 0.760 %, Temperature 23.0 °C

13250 psi

@Strain 0.760 %, Temperature 73.4 °F

DAM; ISO 11403-1 -2
97.16 MPa

@Strain 0.780 %, Temperature -20.0 °C

14090 psi

@Strain 0.780 %, Temperature -4.00 °F

50%RH; ISO 11403-1 -2
98.0 MPa

@Strain 0.897 %, Temperature 40.0 °C

14200 psi

@Strain 0.897 %, Temperature 104 °F

50%RH; ISO 11403-1 -2
98.97 MPa

@Strain 0.800 %, Temperature 0.000 °C

14350 psi

@Strain 0.800 %, Temperature 32.0 °F

DAM; ISO 11403-1 -2
102.66 MPa

@Strain 1.02 %, Temperature 90.0 °C

14890 psi

@Strain 1.02 %, Temperature 194 °F

DAM; ISO 11403-1 -2
104.24 MPa

@Strain 0.910 %, Temperature 40.0 °C

15119 psi

@Strain 0.910 %, Temperature 104 °F

DAM; ISO 11403-1 -2
107 MPa

@Strain 0.882 %, Temperature 0.000 °C

15500 psi

@Strain 0.882 %, Temperature 32.0 °F

50%RH; ISO 11403-1 -2
112.48 MPa

@Strain 1.02 %, Temperature 23.0 °C

16314 psi

@Strain 1.02 %, Temperature 73.4 °F

50%RH; ISO 11403-1 -2
116.13 MPa

@Strain 0.930 %, Temperature -20.0 °C

16843 psi

@Strain 0.930 %, Temperature -4.00 °F

DAM; ISO 11403-1 -2
125.83 MPa

@Strain 1.36 %, Temperature 90.0 °C

18250 psi

@Strain 1.36 %, Temperature 194 °F

DAM; ISO 11403-1 -2
131.27 MPa

@Strain 1.30 %, Temperature 40.0 °C

19039 psi

@Strain 1.30 %, Temperature 104 °F

50%RH; ISO 11403-1 -2
134.89 MPa

@Strain 1.14 %, Temperature 0.000 °C

19564 psi

@Strain 1.14 %, Temperature 32.0 °F

DAM; ISO 11403-1 -2
137.92 MPa

@Strain 1.31 %, Temperature 23.0 °C

20004 psi

@Strain 1.31 %, Temperature 73.4 °F

50%RH; ISO 11403-1 -2
146.77 MPa

@Strain 1.80 %, Temperature 90.0 °C

21287 psi

@Strain 1.80 %, Temperature 194 °F

DAM; ISO 11403-1 -2
153.67 MPa

@Strain 1.28 %, Temperature -20.0 °C

22288 psi

@Strain 1.28 %, Temperature -4.00 °F

DAM; ISO 11403-1 -2
156.27 MPa

@Strain 1.48 %, Temperature 40.0 °C

22665 psi

@Strain 1.48 %, Temperature 104 °F

DAM; ISO 11403-1 -2
156.32 MPa

@Strain 1.66 %, Temperature 40.0 °C

22672 psi

@Strain 1.66 %, Temperature 104 °F

50%RH; ISO 11403-1 -2
159.92 MPa

@Strain 1.46 %, Temperature 23.0 °C

23194 psi

@Strain 1.46 %, Temperature 73.4 °F

DAM; ISO 11403-1 -2
162.15 MPa

@Strain 1.62 %, Temperature 23.0 °C

23518 psi

@Strain 1.62 %, Temperature 73.4 °F

50%RH; ISO 11403-1 -2
177.86 MPa

@Strain 2.09 %, Temperature 40.0 °C

25796 psi

@Strain 2.09 %, Temperature 104 °F

50%RH; ISO 11403-1 -2
181.2 MPa

@Strain 1.65 %, Temperature 0.000 °C

26280 psi

@Strain 1.65 %, Temperature 32.0 °F

DAM; ISO 11403-1 -2
187.3 MPa

@Strain 1.72 %, Temperature 0.000 °C

27170 psi

@Strain 1.72 %, Temperature 32.0 °F

50%RH; ISO 11403-1 -2
189.71 MPa

@Strain 1.97 %, Temperature 40.0 °C

27515 psi

@Strain 1.97 %, Temperature 104 °F

DAM; ISO 11403-1 -2
191.21 MPa

@Strain 1.74 %, Temperature -20.0 °C

27733 psi

@Strain 1.74 %, Temperature -4.00 °F

50%RH; ISO 11403-1 -2
204.28 MPa

@Strain 1.96 %, Temperature 0.000 °C

29628 psi

@Strain 1.96 %, Temperature 32.0 °F

DAM; ISO 11403-1 -2
205.31 MPa

@Strain 2.10 %, Temperature 23.0 °C

29778 psi

@Strain 2.10 %, Temperature 73.4 °F

DAM; ISO 11403-1 -2
210.24 MPa

@Strain 2.06 %, Temperature 0.000 °C

30493 psi

@Strain 2.06 %, Temperature 32.0 °F

50%RH; ISO 11403-1 -2
216.76 MPa

@Strain 2.02 %, Temperature -20.0 °C

31438 psi

@Strain 2.02 %, Temperature -4.00 °F

DAM; ISO 11403-1 -2伸长率 (断裂)2.3 %2.3 %50%RH; ISO 527-1/-2
2.4 %2.4 %DAM; ISO 527-1/-2拉伸模量11.5 GPa1670 ksi50%RH; ISO 527-1/-2
12.0 GPa1740 ksiDAM; ISO 527-1/-2弯曲模量10.0 GPa1450 ksi50%RH; ISO 178
10.5 GPa1520 ksiDAM; ISO 178割线模量1.01 GPa

@Strain 5.47 %, Temperature 200 °C

147 ksi

@Strain 5.47 %, Temperature 392 °F

DAM; ISO 11403-1 -2
1.29 GPa

@Strain 4.02 %, Temperature 200 °C

187 ksi

@Strain 4.02 %, Temperature 392 °F

DAM; ISO 11403-1 -2
1.75 GPa

@Strain 2.63 %, Temperature 200 °C

254 ksi

@Strain 2.63 %, Temperature 392 °F

DAM; ISO 11403-1 -2
2.71 GPa

@Strain 1.30 %, Temperature 200 °C

393 ksi

@Strain 1.30 %, Temperature 392 °F

DAM; ISO 11403-1 -2
4.2425 GPa

@Strain 0.400 %, Temperature 200 °C

615.33 ksi

@Strain 0.400 %, Temperature 392 °F

DAM; ISO 11403-1 -2
7.40 GPa

@Strain 2.54 %, Temperature 40.0 °C

1070 ksi

@Strain 2.54 %, Temperature 104 °F

50%RH; ISO 11403-1 -2
8.70 GPa

@Strain 2.33 %, Temperature 23.0 °C

1260 ksi

@Strain 2.33 %, Temperature 73.4 °F

50%RH; ISO 11403-1 -2